Cu-MOF-derived Cu nanoparticles decorated porous N-doped biochar for low-temperature H2S desulfurization

Hydrogen sulfide (H2S) is a highly toxic and corrosive gas that poses significant risks to human health and the environment. Therefore, the development of an adsorbent capable of efficiently purifying H2S at room temperature remains a challenging task. In this study, a novel composite adsorbent with a specific surface area of 434 m2·g−1 was fabricated by modifying porous N-doped biochar with Cu nanoparticles (Cu/NBC) derived from Cu-MOFs for low-temperature desulfurization of H2S. The effect of pyrolysis temperature and the doping ratio of Cu-MOFs to biochar on the desulfurization performance of H2S for the as-prepared Cu/NBC was comprehensively investigated. Experimental results indicated that the desulfurization capability of the optimized Cu/NBC-600-1 adsorbent (synthesized at a pyrolysis temperature of 600 °C and a doping ratio of 1:1) was significantly affected by the desulfurization conditions, and the optimal conditions were determined to be at 25 °C, with 20 % oxygen content and 70 % relative humidity. Under the optimized conditions, the Cu/NBC-600-1 adsorbent exhibited a high H2S removal capacity of 158.28 mg·g−1, which was about 3.8 times higher than that of the pristine N-doped biochar. The desulfurization mechanism of the Cu/NBC composite was demonstrated to involve reactive adsorption and catalytic oxidation, resulting in the formation of elemental sulfur and copper sulfides as the main products. This study not only provides a promising approach to modify porous biochar with MOF derivatives, but also offers an effective strategy to remove low concentration H2S at room temperature.