Multilayered Shape-Morphing Scaffolds with a Hierarchical Structure for Uterine Tissue Regeneration

Owing to dysfunction of the uterus, millions of couples around the world suffer from infertility. Different from conventional treatments, tissue engineering provides a new and promising approach to deal with difficult problems such as human tissue or organ failure. Adopting scaffold-based tissue engineering, three-dimensional (3D) porous scaffolds in combination with stem cells and appropriate biomolecules may be constructed for uterine tissue regeneration. In this study, a hierarchical tissue engineering scaffold, which mimicked the uterine tissue structure and functions, was designed, and the biomimicking scaffolds were then successfully fabricated using solvent casting, layer-by-layer assembly, and 3D bioprinting techniques. For the multilayered, hierarchical structured scaffolds, poly(l-lactide-co-trimethylene carbonate) (PLLA-co-TMC, "PLATMC" in short) and poly(lactic acid-co-glycolic acid) (PLGA) blends were first used to fabricate the shape-morphing layer of the scaffolds, which was to mimic the function of myometrium in uterine tissue. The PLATMC/PLGA polymer blend scaffolds were highly stretchable. Subsequently, after etching of the PLATMC/PLGA surface and employing estradiol (E2), polydopamine (PDA), and hyaluronic acid (HA), PDA@E2/HA multilayer films were formed on PLATMC/PLGA scaffolds to build an intelligent delivery platform to enable controlled and sustained release of E2. The PDA@E2/HA multilayer films also improved the biological performance of the scaffold. Finally, a layer of bone marrow-derived mesenchymal stem cell (BMSC)-laden hydrogel [which was a blend of gelatin methacryloyl (GelMA) and gelatin (Gel)] was 3D printed on the PDA@E2/HA multilayer films of the scaffold, thereby completing the construction of the hierarchical scaffold. BMSCs in the GelMA/Gel hydrogel layer exhibited excellent cell viability and could spread and be released eventually upon biodegradation of the GelMA/Gel hydrogel. It was shown that the hierarchically structured scaffolds could evolve from the initial flat shape into the tubular structure completely in an aqueous environment at 37(degrees)C, fulfilling the requirement for curved scaffolds for uterine tissue engineering. The biomimicking scaffolds with a hierarchical structure and curved shape, high stretchability, and controlled and sustained E2 release appear to be very promising for uterine tissue regeneration.