Enhanced thermoelectric and mechanical properties of Bi0.5Sb1.5Te3 alloy with dispersed yttrium oxide ceramic nanoparticles

Reducing thermal conductivity while avoiding adverse interfacial reactions during sintering is crucial for improving the thermoelectric performance of Bi2Te3-based composites. Inert ceramic nanoparticles are good candidates for achieving this goal. In this study, we designed and prepared a series of p-type Bi0.5Sb1.5Te3 nanocomposites decorated with Y2O3 ceramic nanoparticles via ball-milling dispersion and spark-plasma sintering. Owing to the chemical stability of the ceramics, no traces of atomic doping or interfacial reactions were observed. Transport measurements revealed that the Y2O3 nanoparticles distributed along the grain boundaries acted as energy-dependent carrier-filtering centers to improve the scattering parameter and Seebeck coefficient, contributing to the elevated power factor even with a decreased electrical conductivity. Moreover, the incorporated Y2O3 nanoparticles and various defect structures they induced effectively strengthened the phonon scattering and suppressed the lattice thermal conductivity. Consequently, a peak figure of merit (ZT) of 1.23 at 313 K was achieved for 0.4