A UV non-hydrogen pure selenite nonlinear optical material for achieving balanced properties through framework-optimized structural transformation

For non-centrosymmetric (NCS) oxides intended for ultraviolet (UV) nonlinear optical (NLO) applications, achieving a wide band gap, large second harmonic generation (SHG) intensity, and sufficient birefringence to satisfy phase matching is a significant challenge due to their inherent incompatibility. To address this issue, this study proposes a strategy called framework-optimized structural transformation. Building upon centrosymmetric (CS) NaGa(SeO3)2 as a foundation, an original UV selenite NLO material, NaLu(SeO3)2, was successfully synthesized. The derived NaLu(SeO3)2 exhibits a balanced comprehensive performance, including a band gap (5.3 eV), an SHG response (2.7 x KDP), a UV cut-off edge (210 nm), a laser-induced damage threshold (LIDT) (151.69 MW cm-2), birefringence (Cal: 0.138@546 nm, Exp: 0.153@546 nm), thermal stability (similar to 575 degrees C) and environmental stability. Notably, its SHG effect, band gap, LIDT, and birefringence are all the largest among UV non-hydrogen pure selenite materials. Such progress can be attributed to the successful arrangement of the SeO3 groups by optimizing the cations on the framework of the parent compound. NCS NaLu(SeO3)2 was designed by framework-optimized structural transformation from CS NaGa(SeO3)2. NaLu(SeO3)2 exhibits large SHG responses, a wide band gap, a short UV cut-off edge, high LIDT, sufficient birefringence and high thermal stability.