The electrocaloric effect of lead-free Ba_1-yCa_yTi_1-xHfxO₃ from direct and indirect measurements

We report on the dielectric and electrocaloric properties of Ba1-yCayTi1-xHfxO3 for compositions 0.12 < x < 0.18 and y = 0.06, as well as x = 0.15 and 0 < y < 0.15, synthesized by the conventional solid-state reaction method. The addition of Hf/Ca broadens the ferroelectric-paraelectric phase transition while moving it toward room temperature. Two interferroelectric transitions are seen to converge, together with the ferroelectric-paraelectric phase transition, at similar to 335 K for 0.12 < x(c) < 0.135 and y = 0.06. Consistent with the dielectric properties, the electrocaloric effect maximizes closer to room temperature with increasing Hf/Ca substitutions, which promote larger temperature spans. The electrocaloric responsivity gradually decreases from 0.2 to 0.1 K mm kV(-1) with the addition of Hf/Ca. A homemade quasi-adiabatic calorimeter is employed to measure "directly" the electrocaloric data, which are also calculated from polarization-versus-electric-field cycles using "indirect" standard procedures. The comparison between measured and calculated values highlights the importance of having access to direct methods for a reliable determination of the electrocaloric effect.(c) 2023 Author(s). All article content, except where otherwise noted, is licensed under a Creative Commons Attribution (CC BY) license(http://creativecommons.org/licenses/by/4.0/).