Surface micromorphology and nanostructures evolution in hybrid laser processes of slicing and polishing single crystal 4H-SiC

Slicing and post-treatment of SiC crystals have been a significant challenge in the integrated circuit and microelectronics industry. To compete with wire-sawing and mechanical grinding technology, a promising approach combining laser slicing and laser polishing technologies has been innovatively applied to increase utilization and decrease damage defects for single crystal 4H-SiC. Significant material utilization has been achieved in the hybrid laser processes, where material loss is reduced by 75% compared to that of conventional machining technologies. Without any special process control or additional treatment, an internally modified layer formed by laser slicing can easily separate the 4H-SiC crystals using an external force of about similar to 3.6 MPa. The modified layer has been characterized using a micro-Raman method to determine residual stress. The sliced surface exhibits a combination of smooth and coarse appearances around the fluvial morphology, with an average surface roughness of over Sa 0.89 pm. An amorphous phase surrounds the SiC substrate, with two dimensions of lattice spacing, d = 0.261 nm and d = 0.265 nm, confirmed by high-resolution transmission electron microscopy (HRTEM). The creation of laser-induced periodic surface nanostructures in the laser-polished surface results in a flatter surface with an average roughness of less than Sa 0.22 pm. Due to the extreme cooling rates and multiple thermal cycles, dissociation of Si-C bonding, and phase separation are identified on the laser-polished surface, which is much better than that of the machining surface. We anticipate that this approach will be applicable to other high-value crystals and will have promising viability in the aerospace and semiconductor industries.(c) 2023 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.