Effects of inherent components and disposal temperature on the melting behavior of petrochemical sludge char during CO₂ gasification

Pyrolysis-coupled gasification-melting is a promising technology as it can dispose of the petrochemical sludge (PS) and recover the leftover energy. Unfortunately, there has been little research investigating the effects of pyrolysis degree on melting characteristics of the pyrolysis residue (PR) and the transformation properties of the heavy metal (HM). In this study, the function of inherent components and disposal temperature were elucidated. The results show that the moisture and light volatile could disperse the melting residue (MR) during gasification -melting treatment, causing different morphology and color of the MR. In addition, as pyrolysis temperature increased, the HMs speciation (e.g. Zn, Cu, and Cr) in the PR was transformed from bioavailable to a stable state, and the yield of PR decreased from 66.8% to 36.5%. The PR produced at 800 degrees C could decrease about 0.9 similar to 1.9 potential ecological risk of releasing substances during the subsequent high-temperature gasification-melting owing to its stable HMs state and less char composition. Moreover, the gasification at 125 degrees C could realize the safe disposal of the PR. Further increasing the gasification temperature to 145 degrees C could not improve the acid -leaching resistance of the HMs, although the apparent concentration of C and the acid dissolution proportion of slag decreased by 6.3% and 1.7%, respectively.