Boosting the CO2 adsorption performance by defect-rich hierarchical porous Mg-MOF-74

Adsorbents with high adsorption capacity and high selectivity are crucial for carbon capture, utilization and storage (CCUS) technology applied to industrial flue gas to reduce carbon emissions. In this paper, a defect-rich hierarchical porous Mg-MOF-74 was synthesized successfully with MgCl2.6H2O used as a metal source considering that the weak coordination of Cl- may interfere with the normal coordination process of metal centers and organic ligands, which causes the formation of crystal defects. Through the analysis of a series of characterizations, ligand deletion of Mg-MOF-74 prepared with MgCl2.6H2O was confirmed, and the deleted ligand was estimated to be approximately 20% compared with the traditional Mg-MOF-74 prepared with Mg(NO3)2.6H2O, which led to mesopores accounting for 36.9%, and the width of mesopores reached 13.1 nm. Compared with traditional Mg-MOF-74, the adsorption heat of CO2 at zero load of the defect-rich hierarchical porous Mg-MOF74 increased from 36 kJ.mol- 1 to 46 kJ.mol- 1, and the saturated adsorption capacity of CO2 under ambient pressure was improved by 15%. Interestingly, the IAST selective adsorption performance of CO2/N2 was increased by 20 times. Compared with the saturated adsorption capacity for traditional Mg-MOF-74, the equivalent adsorption capacity of hierarchical porous Mg-MOF-74 only needs 17 kPa, indicating that it is suitable for carbon capture operation in a real flue environment. Calculations of density functional theory (DFT) confirmed that the active site of the hierarchical porous Mg-MOF-74 has a lower adsorption energy with CO2 due to the presence of defects, which is regarded to play a key role in improving the CO2 capture performance.