Influence of boron bearing fillers on flame retardancy properties of huntite hydromagnesite filled ductile PLA biocomposites Bor içeren dolgu maddelerinin huntit hidromagnezit içeren sünek PLA biyokompozitlerde alev geciktirici özelliklerine etkisi

In this work, the flame retardant influences of colemanite and boron oxide are investigated in huntite-hydromagnesite (HH) containing plasticized poly (lactic acid) (PLA) biocomposites. The composites are characterized using limiting oxygen index (LOI), horizontal (UL 94 HB) and vertical (UL-94 V) burning tests, mass loss calorimeter and thermo gravimetric analysis (TGA). The addition of colemanite causes enhanced fire retardant performance with higher UL-94 V rating and LOI value and lower pHRR value. V0 rating and the highest LOI value is observed with the addition 1 wt % colemanite. When the concentration of colemanite reaches to 3 and 5 wt %, the samples get V1 rating. When the concentration of colemanite reaches to 5 wt %, pHRR and avHRR values are lower than those of the reference sample. The addition of boron oxide caused only improvement in LOI value. The highest LOI value (33.2) is observed in 5 and 10 wt % boron oxide containing samples.