High-toughness mullite ceramics fabricated by hot-press sintering of pyrophyllite and AlOOH at low temperatures

High-toughness mullite ceramics were fabricated through hot-press sintering (HPS) of pyrophyllite and AlOOH, which were wet-milled and well mixed using a planetary ball mill. The impacts of sintering temperatures and contents of AlOOH on mullite phase formation, densification, microstructure and mechanical properties in ceramic materials were investigated through XRD, SEM and mechanical properties determination. The results indicated that high-toughness mullite ceramics could be successfully prepared by HPS at temperatures higher than 1200 degrees C for 120 min. Increasing the sintering temperature from 1000 to 1300 degrees C significantly enhanced the flexural strength and fracture toughness of samples. The highest flexural strength of 297.97 +/- 25.32 MPa and fracture toughness of 4.64 +/- 0.11 MPa center dot m(1/2) were obtained for samples sintered at 1300 degrees C. Further increase of temperature to 1400 degrees C resulted in slight decrease of flexural strength and fracture toughness. Compared with the mullite ceramics prepared only using pyrophyllite as raw material, incorporation of AlOOH into raw material significantly increased the mechanical properties of final mullite ceramics. And stoichiometric AlOOH and pyrophyllite as starting material gave the best performance in fracture toughness. The high-toughness of mullite ceramics were ascribed to the high mullite phase content, fine mullite whiskers and in situ formed, intertwined three-dimensional network structure obtained through HPS at a low temperature of 1300 degrees C.