The synergistic effect of heterogeneous nucleation and stress-induced crystallization on supramolecular structure and performances of poly(lactic acid) melt-spun fibers.

As a kind of bio-based polymer, poly (lactic acid) has potential application in fibers fields. Due to the weak nucleation ability, PLA crystallizes slowly and forms large spherulites during the forming process, which deteriorates the properties of PLA fibers. In this work, melt-spun method is employed for the fabrication of PLA/T composite fibers using succinate diphenyl dihydrazide (TMC-306) as the nucleating agent, and then the hot-drawing and heat setting is performed to the as-spun fibers. Compared with pure PLA fibers, PLA/T fibers show faster crystallization rate and improved performance due to the synergistic effect of heterogeneous nucleation and stress-induced crystallization. The characterization of non-isothermal crystallization behavior indicates that the peak crystallization temperature as well as crystallinity of PLA composites is increased to 121.5 °C and 36.78 % respectively by blending 0.3 wt% TMC-306. Meanwhile, the obtained PLA/0.3T composite fibers are highly crystallized and oriented at hot-drawing ratio of 2.4 folds and heat setting temperature of 100 °C, and the conformational stability is noticeably enhanced. Further, the tensile strength and storage modulus of PLA/0.3T composite fiber are 3.46 cN/dtex and 46,953 MPa respectively, which are increased by 42 % and 41 % compared with neat PLA fibers.