Microstructure and corrosion resistance of highly 111 oriented electrodeposited CoNiFe medium-entropy alloy films

The medium-entropy alloy is a newly intriguing material showing superb properties. A simple, one-step method was developed to electrodeposit CoNiFe medium-entropy alloy films from a sulfate and citrate bath. The microstructure and corrosion resistance were investigated in CoNiFe films with varying deposition current densities. It shows the facecentered cubic structure with a <111> preferential orientation. HRTEM-EDS observations further show information on the nanostructure and element distribution. The films exhibit a strong corrosion resistance in 3.5 wt.% NaCl solution. The films electrodeposited with a current density of 44.4 A/dm2 shows a low self-corrosion current density of 4.72 x 10-6 A,cm_2 in 3.5 wt.% NaCl solution. The corrosion mechanism was proposed in combination with electrochemical impedance spectroscopy results. The outstanding properties were attributed to the near-equimolar ternary components. The results lay a solid foundation for developing of highly oriented medium-entropy alloy films with strong corrosion resistance. (c) 2022 The Author(s). Published by Elsevier B.V. This is an open access article under the CC