Synthesis of Magnetic α-Fe2O3/Rutile TiO2 Hollow Spheres for Visible-Light Photocatalytic Activity

The high recombination rate of the electron-hole pair on the surface of rutile TiO2 (RT) reduces its photocatalytic performance, although it has high thermodynamic stability and few internal grain defects. Therefore, it is necessary for RT to develop effective methods to reduce electron-hole pair recombination. In this study, magnetic α-Fe2O3/Rutile TiO2 self-assembled hollow spheres were fabricated via a facile hydrothermal reaction and template-free method. Based on the experimental result, phosphate concentration was found to play a crucial role in controlling the shape of these hollow α-Fe2O3/RT nanospheres, and the optimal concentration is 0.025 mM. Due to a heterojunction between α-Fe2O3 and RT, the electron-hole pair recombination rate was reduced, the as-synthesized hollow α-Fe2O3/RT nanospheres exhibited excellent photocatalysis in rhodamine B (RhB) photodegradation compared to α-Fe2O3 and RT under visible-light irradiation, and the degradation rate was about 16% (RT), 60% (α-Fe2O3), and 93% (α-Fe2O3/RT) after 100 min. Moreover, α-Fe2O3/RT showed paramagnetism and can be recycled to avoid secondary environmental pollution.