Influence Of Pore-Size/Porosity On Ion Transport And Static Bsa Fouling For Tio2-Covered Nanoporous Alumina Membranes

The influence of geometrical parameters (pore radii and porosity) on ion transport through two almost ideal nanoporous alumina membranes (NPAMs) coated with a thin TiO2 layer by the atomic layer deposition technique (Sf-NPAM/TiO2 and Ox-NPAM/TiO2 samples) was analyzed by membrane potential and electrochemical impedance spectroscopy measurements. The results showed the significant effect of pore radii (10 nm for Sf-NPAM/TiO2 and 13 nm for Ox-NPAM/TiO2) when compared with porosity (9% and 6%, respectively). Both electrochemical techniques were also used for estimation of protein (bovine serum albumin or BSA) static fouling, and the results seem to indicate deposition of a BSA layer on the Sf-NPAM/TiO2 fouled membrane surface but pore-wall deposition in the case of the fouled Ox-NPAM/TiO2 sample. Moreover, a typical and simple optical technique such as light transmission/reflection (wavelength ranging between 0 and 2000 nm) was also used for membrane analysis, showing only slight transmittance differences in the visible region when both clean membranes were compared. However, a rather significant transmittance reduction (similar to 18%) was observed for the fouled Sf-NPAM/TiO2 sample compared to the fouled Ox-NPAM/TiO2 sample, and was associated with BSA deposition on the membrane surface, thus supporting the electrochemical analysis results.