Quasi-Ionic Liquid Enabling Single-Phase Poly(Vinylidene Fluoride)-Based Polymer Electrolytes For Solid-State Lini0.6co0.2mn0.2o2 Parallel To Li Batteries With Rigid-Flexible Coupling Interphase

Poly(vinylidene fluoride)-based polymer electrolytes are being intensely investigated for solid-state lithium metal batteries. However, phase separation and porous structures are still pronounced issues in traditional preparing procedure. Herein, a bottom-to-up strategy is employed to design single-phase and densified polymer electrolytes via incorporating quasi-ionic liquid with poly(vinylidene fluoride-co-hexafluoropropylene). Due to strong ion/dipole-dipole interaction, the optimized polymer electrolyte delivers high room-temperature ionic conductivity of 1.55 x 10(-3) S cm(-1), superior thermal and oxidation stability of 4.97 V, excellent stretchability of over 1500% and toughness of 43 MJ cm(-3) as well as desirable self-extinguishing ability. Furthermore, the superb compatibility toward Li anode enables over 3000 h cycling of Li plating/stripping and approximate to 98% Coulombic efficiency in Li parallel to Cu test at 0.1 mA cm(-2). In particular, lithium metal battery Li parallel to LiNi0.6Co0.2Mn0.2O2 exhibits a room-temperature discharge retention rate of 96% after 500 cycles under a rate of 0.1 C, which is associated with the rigid-flexible coupling electrodes/electrolytes interphase. This investigation demonstrates the potential application of quasi-ionic liquid/polymer electrolytes in safe lithium metal batteries.