Effect Of Tio2 Addition On Grain Growth, Anodic Bubble Evolution And Anodic Overvoltage Of Nife2o4-Based Composite Inert Anodes

A two-step powder compaction and sintering process was employed to fabricate TiO2-doped NiFe2O4 ceramic-based inert anodes. Grain growth during isothermal sintering was analyzed using Brook grain growth model. The bubble behavior of NiFe2O4 ceramic-based inert anodes was investigated in a twocompartment see-through quartz cell for aluminum electrolysis process. Anodic overvoltage and potential decay curves of the inert anodes were measured by using the steady state and current interruption technique. The results showed that the kinetic index of grain growth decreased with an increase in temperature. The average activation energy of grain growth for 1.0 wt.% TiO2-doped NiFe2O4 ceramic samples with a sintering temperature range from 1373 to 1673 K dropped from 675.30 to 183.47 kJ/mol. The diameter size of bubbles before releasing from the bottom surface of the anodes was reduced with increasing the current density, and the larger average releasing bubble size for carbon anode at the same current density could be obtained, which was compared to the NiFe2O4 inert anodes. Besides, the cell voltage of carbon anodes fluctuated much more violently under the same experimental conditions. After adding small amount of TiO2, a minor reduction in anodic overvoltage of NiFe2O4-based anodes can be observed.