Effect Of Intra-Ply Voids On The Homogenized Behavior Of A Ply In Multidirectional Laminates

This work focuses on the effect of intra-ply voids on the homogenized nonlinear behavior of a ply in multidirectional composites. Voids were modeled explicitly on the fiber scale and linked to the ply-scale by the recently developed two-scale framework which couples Classical Laminate Theory on the macro-scale with Finite Element analysis on the micro-scale. Laminates [+/- 45](2s) and [+/- 67.5](2s) were used as validation cases. The computed homogenized behavior of plies with and without voids for each laminate were compared against existing experimental data on manufactured plates. The nonlinearity of the homogenized stress-strain curves of all models is in a good agreement with experiments up to 1% of applied deformation for a laminate [+/- 45](2s) and up to 0.4% for a laminate [+/- 67.5](2s). The effect of voids was assessed only virtually and it is shown that 4% of void content decreases the ply strength by 30%, transversal Young's and shear moduli by around 10% and 8% respectively, whereas longitudinal stiffness is only slightly affected by the presence of voids. This work is the first step towards automatization of the virtual identification of the complete set of damage-plasticity parameters for the LMT-Cachan damage model accounting for the presence of intra-ply voids.