Epitaxial Growth And Determination Of Band Alignment Of Bi2te3-Wse2 Vertical Van Der Waals Heterojunctions

Artificial heterojunctions formed by vertical stacking of dissimilar two-dimensional (2D) transition metal dichalcogenide (TMD) monolayer materials in a chosen sequence hold tantalizing prospects for futuristic atomically thin circuits. The emergence of 2D topological insulators (TI), including Bi2Te3, Bi2Se3, and Sb2Te3, represents a new class of 2D building blocks and can complement the existing artificial heterojunctions as a result of their intriguing surface states protected by the time-reversal symmetry. However, the determination of band alignments of such 2D TI/TMD vertical heterojunctions, the key parameter for designing HJ-based electronic/photonic devices, which lies in the development of epitaxy growth, remains in its infancy. Here, we demonstrate the epitaxy growth of 2D TI/TMD vertical heterojunctions comprised of Bi2Te3/WSe2 with atomically clean interfaces that are spectroscopically accessible, and theoretically tractable. Cross-sectional scanning transmission electron microscopy (STEM) images and the presence of interlayer-coupled characteristics from Raman spectroscopy collectively confirm the neat stacking of Bi2Te3/WSe2 with the absence of unwa nted containments. Microbeam X-ray photoelectron spectroscopy (mu XPS) measurement coupled with the density functional theory (DFT) calculations and electrical characteristics of field effect transistors quantitatively reveals the type-II alignment of vertically stacked of quintuple layers (QL) Bi2Te3/WSe2. Meanwhile, the type-III band emerges when transitioning to multi-quintuple layer (MQL) Bi2Te3/WSe2. The finding here provides a well-defined example of the epitaxy growth paradigm, the interlayer coupling-electronic properties relationship, for these emerging 2D TI/TMDs vertical heterojunctions.