The spin-orbit-phonon coupling and crystalline elasticity of LaCoO3 perovskite

Based on an integrated study of magnetic susceptibility, specific heat, and thermal expansion of single-crystal LaCoO3 free from cobalt and oxygen vacancies, two narrow spin gaps are identified before and after the phonon softening of gap size Delta E similar to 0.5 meV in a CoO6-octahedral crystal electric field (CEF) and the thermally activated spin gap Q similar to 25 meV, respectively. Significant excitation of Co3+ spins from a low-spin (LS) to a high-spin (HS) state is confirmed by the thermal activation behavior of spin susceptibility chi(S) of energy gap Q similar to 25 meV, which follows a two-level Boltzmann distribution to saturate at a level of 50% LS/50% HS statistically above similar to 200 K, without the inclusion of a postulated intermediate spin (IS) state. A threefold increase in the thermal expansion; coefficient (alpha) across the same temperature range as that of thermally activated HS population growth is identified, which implies the non-trivial spin-orbit-phonon coupling caused the bond length of Co3+(LS <-> HS)-O fluctuation and the local lattice distortion. The unusually narrow gap of Delta E similar to 0.5 meV for the CoO6 octahedral CEF between e(g)-t(2g) indicates a more isotropic negative charge distribution within the octahedral CEF environment, which is verified by the Electron Energy Loss Spectroscopy (EELS) study to show nontrivial La-O covalency.