Complete Fabrication of a Traversable 3 mu m Thick NbN Film Superconducting Coil with Cu plated layer of 42m in Length in a Spiral Three-Storied Trench Engraved in a Si Wafer of 76.2 mm in Diameter Formed by MEMS Technology for a Compact SMES with High Energy Storage Volume Density

Based on the concept of a novel approach to make a compact SMES unit composed of a stack of Si wafers using MEMS process proposed previously, a complete fabrication of a traversable 3 mu m thick NbN film superconducting coil lined with Cu plated layer of 42m in length in a spiral three-storied trench engraved in and extended over a whole Si-wafer of 76.2 mm in diameter was attained for the first time. With decrease in temperature, the DC resistivity showed a metallic decrease indicating the current pass was in the Cu plated layer and then made a sudden fall to residual contact resistance indicating the shift of current pass from the Cu plated layer to the NbN film at the critical temperature Tc of 15.5K by superconducting transition. The temperature dependence of I-V curve showed the increase in the critical current with decrease in the temperature and the highest critical current measured was 220 mA at 4K which is five times as large as that obtained in the test fabrication as the experimental proof of concept presented in the previous report. This completion of a one wafer superconducting NbN coil is an indispensable step for the next proof of concept of fabrication of series-connected two wafer coils via superconductive joint which will read to series connected 600 wafer coils finally, and for replacement of NbN by high T-c superconductor such as YBa2Cu3O7-x for operation under the cold energy of liquid hydrogen or liquid nitrogen.