Room Temperature Wafer-Scale Synthesis Of Highly Transparent, Conductive Cus Nanosheet Films Via A Simple Sulfur Adsorption-Corrosion Method

The development of highly conductive electrodes with robust mechanical durability and clear transmittance in the visible to IR spectral range is of great importance for future wearable/flexible electronic applications. In particular, low resistivity, robust flexibility, and wide spectral transparency have a significant impact on optoelectronic performance. Herein, we introduce a new class of covellite copper monosulfide (CuS) nanosheet films as a promising candidate for soft transparent conductive electrodes (TCEs). An atmospheric sulfur adsorption-corrosion phenomenon represents a key approach in our work for the achievement of wafer-scale CuS nanosheet films through systematic control of the neat Cu layer thickness ranging from 2 to 10 nm multilayers at room temperature. These nanosheet films provide outstanding conductivity (similar to 25 Omega sq(-1)) and high transparency (> 80%) in the visible to infrared region as well as distinct flexibility and long stability under air exposure, yielding a high figure-of- merit (similar to 60) that is comparable to that of conventional rigid metal oxide material-based TCEs. Our unique room temperature synthesis process delivers high quality CuS nanosheets on any arbitrary substrates in a short time (< 1 min) scale, thus guaranteeing the widespread use of highly producible and scalable device fabrication.