Free-standing, flexible, electrically conductive epoxy/graphene composite films Part A Applied science and manufacturing

Cost-effective, solution-processable and high-quality nanomaterials have critical roles in the development of advanced polymer composite films which combine mechanical robustness with functional properties such as electrical conductivity for many applications. This study first fabricated 3nm-thick graphene platelets (GnPs) which have an electrical conductivity of 1460S/cm; each platelet may contain double or a few layers of graphene whose C/O ratio was measured as 13.2. We then developed epoxy/GnP composite films by a layer-by-layer method through two-step curing. A percolation threshold of electrical conductivity was observed at merely 0.6vol% GnPs, and the composite electrical conductivity increased to 1298.7S/cm at 20.0vol%. The composite films were mechanically strong to be used as the cost-effective electrodes for flexible supercapacitors. Specific capacitance 50.1F/g was recorded for the 15.0vol% composite film by two-electrode configuration, in comparison with the specific capacitance 41F/g for commercial multi-walled carbon nanotubes. More importantly, impressive capacitance was found at a high current density of 20A/g, which is desired in practical applications. The film electrode demonstrated a capacitance retention rate of 94.7% through 20,000 cycles. At a bending angle of 90°, it exhibited a capacitance of 38.9F/g at 100mV/s.