Pore structure and properties of poly(ether ether ketone) hollow fiber membranes: influence of solvent‐induced crystallization during extraction

Poly(ether ether ketone) (PEEK) hollow fiber membranes were prepared by a thermally induced phase separation method with polyetherimide as diluent, and N-methyl pyrrolidone (NMP), dichloromethane and a composite extractant composed of NMP, ethanolamine and water as extractant. The effects of the different solvents induced crystallization on the pore structure during extraction and the properties of the PEEK hollow fiber membranes were investigated in detail. The crystallization behaviors of the membranes were characterized by DSC and XRD. The effect of the extractants on the microscopic morphologies, pore structures, water fluxes and mechanical properties of the membranes were investigated. The results showed that the extraction ability of the composite extractant was the most significant, followed by NMP and dichloromethane. The crystallinity of the hollow fiber was 39.0% before extraction and was elevated to 39.2% after the extraction with NMP, 46.6% with dichloromethane and 46.7% with the composite extractant, which shows that dichloromethane and the composite extractant have strong ability to induce the crystallization of PEEK. The inner and outer surfaces of the membranes obtained after extraction by the composite extractant had the largest pore size and the highest surface porosity. The most probable pore diameter of the membranes obtained after extraction by NMP, dichloromethane and the composite extractant was 23.26 nm, 24.43 nm and 24.43 nm, respectively, which indicated that solvent-induced crystallization was beneficial for the formation of larger pores. The pure water flux of the PEEK membrane prepared by the composite extractant was the largest, but the tensile strength was the lowest. (c) 2019 Society of Chemical Industry