Twin Interactions in Pure Ti Under High Strain Rate Compression

Twin interactions associated with 11 2 1 (E2) twins in titanium deformed by high strain rate ( 2600 s −1 ) compression were studied using electron backscatter diffraction technique. Three types of twins, 10 1 2 (E1), 11 2 2 (C1), and 11 2 4 (C3), were observed to interact with the preformed E2 twins in four parent grains. The E1 variants nucleated at twin boundaries of some E2 variants. And the C3 twins were originated from the intersection of C1 and E2. The selection of twin variant was investigated by the Schmid factors (SFs) and the twinning shear displacement gradient tensors (DGTs) calculations. The results show that twin variants that did not follow the Schmid law were more frequently observed under high strain rate deformation than quasi-static deformation. Among these low-SF active variants, 73 pct (8 out of 11) can be interpreted by DGT. Besides, 26 variants that have SF values close to or higher than their active counterparts were absent. Factors that may affect the twin variant selections were discussed.