Study of the Al-Si-X system by different cooling rates and heat treatment

The solidification behavior of the Al-12.6% Si (A1), the hypereutectic Al-20%Si (A2) and the Al-20%Si-1.5% Fe-0.5%Mn (A3) (in wt. (%)) alloys, at different cooling rates is reported and discussed. The cooling rates ranged between 0.93 degrees C/s and 190 degrees C/s when cast in sand and copper wedge-shaped molds, respectively. A spheroidization heat treatment was carried out to the alloys in the as-cast condition at 540 degrees C for 11 hours and quench in water with a subsequent heat treatment at 170 degrees C for 5 hours with the purpose of improving the mechanical properties. The samples were characterized by optical microscopy, scanning electron microscopy and mechanically by tensile test, in order to evaluate the response of the heat treatment on the different starting microstructures and mechanical properties. It was found that alloys cooled at rates greater than 10.8 degrees C/s had a smaller particle size and better distribution, also showed a greater response to spheroidization heat treatment of all silicon (Si) phases. The spheroidization heat treatment caused an increase in the ultimate tensile stress (UTS) and elongation when compared with the alloys in the as-cast condition. The highest UTS value of 174 MPa was obtained for the (A1) alloy.