Nanoscale patterning induced strain redistribution in ultrathin strained Si layers on oxide.

We present a comparative study of the influence of the thickness on the strain behavior upon nanoscale patterning of ultrathin strained Si layers directly on oxide. The strained layers were grown on a SiGe virtual substrate and transferred onto a SiO2/Si substrate using wafer bonding and hydrogen ion induced exfoliation. The post-patterning strain was evaluated using UV micro-Raman spectroscopy for thin ( 20 nm) and thick ( 60 nm) nanostructures with lateral dimensions in the range of 80-400 nm. We found that about 40-50% of the initial strain is maintained in the 20 nm thick nanostructures, whereas this fraction drops significantly to similar to 2-20% for the 60 nm thick ones. This phenomenon of free surface induced relaxation is described using detailed three-dimensional finite element simulations. The simulated strain 3D maps confirm the limited relaxation in thin nanostructures. This result has direct implications for the fabrication and manipulation of strained Si nanodevices.