Exploring the Thermal Behavior and Diffusive Functionality of Structural Defects and Phase Boundaries in Near-Stoichiometric Chromium Diborides by in Situ Scanning Transmission Electron Microscopy

Near-stoichiometric chromium diboride films were subject to in situ annealing inside a scanning transmission electron microscope to access the thermal behavior of the film and embedded structural planar defects. Independent of films' stoichiometry, the planar defects were unaffected by the applied heat treatments. On the contrary, the interfaces between the boron-rich tissue phase and the CrB2 phase were reshaped in the overstoichometric CrB2 film. At high temperatures, diffusion of contact metal species (platinum) from the focused ion beam sample preparation was triggered, with subsequent migration onto the sample. This resulted in the formation of metal-rich regions as directly observed and characterized at the atomic level. We determined that platinum did not react with the diboride structure but is accommodated by various defects present in the film.