Reconciling Inherent Interfacial Compatibility Conflict Enhances Adhesive Infiltration and Resolves Dentin Bonding Durability

Wet bonding is a basic technique used daily in clinics for tooth-restoration fixation. However, only 50% of the bonding lasts more than 5 years and thus patients must visit the dentists repeatedly. This is attributed to the limited infiltration of adhesives into the demineralized dentin (DD) matrix during wet-bonding. Herein, we show that reconciling interfacial compatibility conflict between the DD matrix and the critical hydrophobic adhesive molecules via hydrophobizing the DD matrix enables the adhesives to thoroughly infiltrate and uniformly distribute within the DD matrix. Thus, the bonding of the hydrophobic DD matrix using commercial dentin adhesives achieves the bonding strength 2-6 times higher than that of the non-treated DD matrix. When a hydrophobic adhesive is applied on the hydrophobic DD matrix, a flawless hybrid layer is produced as observed by nanoleakage investigation. A long-term bonding strength comes up to 7.3 fold that of the control group and very importantly, with no attenuation after 12 months. This study clarifies the basic cause of poor wet-bonding durability and demonstrates a paradigm in adhesive dentistry to overcome the long-existing bonding durability problem associated with inadequate adhesive infiltration into the DD matrix. This provides a new angle of view to resolve clinical dentin bonding durability problem and will significantly promote adhesive dentistry. Highlights 1. Inherent interfacial compatibility conflict between demineralized dentin matrix and hydrophobic molecules of dentin adhesives is the basic cause for the dentin bonding durability problem. 2. Reconciling the interfacial compatibility conflict markedly facilitates adhesive infiltration in the demineralized dentin matrix and greatly enhances bonding effectiveness. 3. High interfacial compatibility produces a flawless hybrid layer and ideal bonding effectiveness and durability. ![Figure][1] For wet bonding, poor infiltration of adhesives within the DD matrix inevitably produces numerous defects throughout the hybrid layer, which always leads to the failure of restoration. Via hydrophobizing the DD matrix, reconciling interfacial compatibility conflict between the DD matrix and the hydrophobic adhesive monomers overcomes durability problems associated with the infiltration of adhesives into the DD matrix producing a flawless hybrid layer and providing ideal bonding effectiveness and durability. ### Competing Interest Statement The authors have declared no competing interest. [1]: pending:yes