Performance and Degradation of Electrolyte Supported SOECs with Advanced Thin-Flm Gadolinium Doped Ceria Barrier Layers in Long-Term Stack Test

Abstract Electrolyte supported Solid Oxide Cells (ESCs) with advanced thin-film Gd-doped ceria diffusion barrier layers between electrolyte and electrodes were assembled and electrochemically investigated in a so-called “rainbow” stack with 30 repeat units (RUs). The barrier layers were deposited onto the electrolyte supports via electron-beam physical evaporation deposition (EB-PVD) method at 600 oC. At the initial stage of the SOEC operation, the stack reached a high performance with an electrical efficiency of 99.65% at 75% steam conversion and a total power input of 1.98 kW. A long-term stack test was performed in SOEC mode for over 5000 h and demonstrated a low voltage degradation of approx. +11.3 mV·kh–1 per RU (+0.9% kh–1). The RUs with EB-PVD GDC thin-films revealed similar initial performance and degradation rate to the state-of-the-art cells with screen printed GDC layers. In this paper, the investigation mainly focuses on the electrochemical characteristics of RUs containing the EB-PVD thin-film GDC layers.