Designing a Se-intercalated MOF/MXene-derived nanoarchitecture for advancing the performance and durability of lithium-selenium batteries.

Lithium-selenium batteries have emerged as a promising alternative to lithium-sulfur batteries due to their high electrical conductivity and comparable volume capacity. However, challenges such as the shuttle effect of polyselenides and high-volume fluctuations hinder their practical implementation. To address these issues, we propose synthesizing Fe-CNT/TiO2 catalyst through high-temperature sintering of an amalgamated nanoarchitecture of carbon nanotubes decorated metal-organic framework (MOF) and MXene, optimized for efficient selenium hosting, leveraging the distinctive physicochemical properties. The catalytic features inherent in the porous Se@Fe-CNT/TiO2 nanoarchitecture were instrumental in promoting efficient ion and electron transport, and lithium-polyselenide kinetics, while its inherent porosity could play a crucial role in inhibiting electrode stress during cycling. This nanoarchitecture exhibits remarkable battery performance, retaining 99.7% of theoretical capacity after 425 cycles at 0.5 C rate and demonstrating 95.8% capacity retention after 2000 cycles at 1 C rate, with ∼100% Coulombic efficiency. Additionally, the Se@Fe-CNT/TiO2 electrode exhibited an impressive recovery of 297.5 mAh/g (97.9%) capacity after undergoing 450 cycles at a charging rate of 10 C and a discharging rate of 1 C. This synergistic integration of MOF- and MXene-derived materials unveils new possibilities for high-performance and durable LSeBs, thus advancing electrochemical energy storage systems.