Preparation and Properties of Soft-/Hard-Switchable Transparent Wood with 0 C as a Boundary

Transparent wood has excellent optical and thermal properties and has great potential utilization value in energy-saving building materials, optoelectronic devices, and decorative materials. In this work, transparent wood with soft-/hard-switchable and shape recovery capabilities was prepared by introducing an epoxy-based polymer with a glass transition temperature of about 0 degrees C into the delignified wood template. The epoxy resin was well filled in the pore structure of the delignified wood, and the as-prepared wood exhibited excellent transparency; the optical transmittance and haze of the transparent wood with a thickness of 2.0 mm were approximately 70% and 95%, respectively. Because the glass transition temperature of the epoxy-based polymer was about 0 degrees C, the prepared transparent wood was rigid below 0 degrees C and flexible above degrees C; meanwhile, the transparent wood exhibited shape change and shape recovery properties. Incorporating optical transparency and soft-/hard-switchable ability into the transparent wood opens a new avenue for developing advanced functional wood-based materials.