Preparation and ablation behavior of a ZrB2-SiC coating-matrix integrated C/C composite

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY(2024)

引用 0|浏览3
暂无评分
摘要
The preparation of a ZrB2-SiC coating-matrix integrated C/C composite was achieved by a slurry method and precursor infiltration and pyrolysis. The obtained composites consisted of a SiC outer layer, a ZrB2-SiC inner layer and a C/C-ZrB2-SiC substrate. Compared with a composite without the ZrB2-SiC layer, the mass ablation rates of the composite were reduced by 14.8 %, 12.0 %, and 19.4 %, and the linear ablation rates were reduced by 41.3 %, 28.2 %, and 14 %, respectively, after ablation under an oxyacetylene flame with a heat flux of 4.18 MW/m2 for 60 s, 120 s, and 300 s. During the ablation process, the SiC outer layer played a role in reducing the heating rate and surface temperature and promoting the sintering of ZrO2 so that the oxide layer avoided peeling off under large thermal stress. The ZrB2-SiC inner layer acted as an oxygen, heat and flow barrier, reducing the oxidation rate of the substrate.
更多
查看译文
关键词
Ceramic matrix composite,Microstructure,Ablation resistance
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要