Flexible biopolymer-assisted 3D printed bioceramics scaffold with high shape adaptability

Bioceramics are widely used in bone tissue engineering, yet the inherent high brittleness and low ductility of the ceramics lead to poor machinability, which restricts their clinical applications. Here, a flexible and processable 3D printed bioceramic scaffold with high ceramic content (66.7 %) and shape fidelity (volume shrinkage rate < 5 %) was developed by freeze-thaw cycles, which was assisted by polyvinyl alcohol (PVA) and silk fibroin (SF). The hydrogen bonding between PVA imparted printability to the ceramic ink and enabled the subsequent formation of flexible scaffolds, which can be twisted, bend and cut to match bone defects. After adding SF, the printability of the inks and hydrophilicity of the scaffolds were enhanced, owing to the interactions between PVA and SF. Further, combined with the formation of β-sheet in SF, the scaffolds exhibited superior mechanical strength and excellent thermal stability, and can fully recover at 35 % compressive strain, which was breaking through the brittleness bottleneck of conventional ceramic scaffolds. Moreover, in vitro experiments showed excellent mineralization ability, osteogenic and angiogenic activities of the scaffolds, demonstrating its potential in bone regeneration. This initial study offers a promising personalized material for bone repair that can be used rapidly during surgery.