Physical Characteristics of Sintered Silver Nanoparticle Inks with Different Sizes during Furnace Sintering

The influence of nanoparticle (NP) size on the physical characteristics of sintered silver NP ink was studied using four different types of inks. The Ag NP inks were spin-coated on glass substrates with an average thickness of 300 nm. Each sample was sintered for 30 min, with temperatures from 50 degrees C to 400 degrees C by an interval of 50 degrees C. After sintering, the specific resistance of each case was obtained using the resistance and surface profile measurements. The minimum specific resistance obtained by the experiment was 2.6 mu omega center dot cm in the case in which 50 nm-sized Ag NP ink was sintered at 350 degrees C. The transformed surface morphology and grain size of each case were observed using scanning electron microscopy and atomic force microscopy. The results of this study can be a reference for future manufacturers in selecting the Ag NP size and the sintering temperature.