Molecular structure regulation of FCCs enabling N/S co-doped hollow amorphous carbon with enlarged interlayer spacing and rich defects for superior potassium storage

Constructing high-performance and low-cost carbon anodes for potassium-ion batteries (PIBs) is highly desirable but faces great challenges. In this study, we present a novel approach to fabricating N/S co-doped hollow amorphous carbon (LNSHAC) for superior potassium storage through a template-assisted molecular structure regulation strategy. By tailoring a 3D crosslinked aromatics precursor from fluid catalytic cracking slurry (FCCs), the LNSHAC features a N/S co-doped hollow structure with enlarged interlayer spacing of up to 0.405 nm and rich defects. Such unique microstructure offers fast transport channels for K-ion intercalation/deintercalation and provides more active sites, leading to boosted reaction kinetics and potassium storage capacity. Consequently, the LNSHAC electrode delivers an impressive reversible capacity (466.2 mAh g−1 at 0.1 A/g), excellent rate capability (336.3 mAh g−1 at 2 A/g), and superior cyclic performance (256.9 mAh g−1 after 5000 cycles at 5 A/g with admirable retention of 76.9 %), standing out among the reported carbon-based anodes. When KFeHCF is employed as the cathode, the LNSHAC-based K-ion full cell exhibits a high reversible capacity of 176.6 mAh g−1 at 0.1 A/g and excellent cyclic stability over 200 cycles. This work will inspire the development and application of advanced carbon-based materials for potassium electrochemical energy storage.