Anti-thermal quenching of luminescence in Y₂W₃O₁₂:Yb³⁺/RE³⁺ (RE = Er/Ho/Tm) and its temperature sensing application

Herein, a series of Y2W3O12:10%Yb3+/x%RE3+ (RE = Er/Ho/Tm) phosphors is prepared via a solid-state reaction. The upconversion and downshift luminescence properties of the phosphors were investigated under an excitation of 980 nm. The bright blue light emission from Tm3+ ion and the green and red light emissions from Ho3+(Er3+) ions were observed. The near-infrared light intensity of NIR-I (Tm3+, similar to 850 nm), NIR-II (Er3+: similar to 1550 nm; Tm3+: similar to 1783 nm) and NIR-III (Ho3+: similar to 2050 nm) were analyzed. In particular, the dramatic thermal enhancement phenomenon in visible and NIR regions was exhibited by the Y2W3O12:10%Yb3+/x%RE3+ (RE = Er/Ho/Tm) phosphors. Among them, the green light intensity of Er3+ ions increased 26.77 times, from 303 to 573 K. The NIR-II emission band (similar to 1783 nm) intensity of Tm3+ ions at 533 K increased 168.7 times compared to that at 313 K. The possible thermal enhancement mechanism is illustrated by the negative thermal expansion (NTE) and Frenkel defect of the Y2W3O12 host. Finally, the optical temperature sensing performances of Y2W3O12:10%Yb3+/x%RE3+ (RE = Er/Ho/Tm) samples are investigated according to the luminescence intensity dependence relationship on temperature. The maximum value of S-R reached 4.24% K-1 at 353 K for Y2W3O12:10%Yb3+/0.6%Ho3+ phosphor. The results indicate that the Y2W3O12:10%Yb3+/x%RE3+ (RE = Er/Ho/Tm) phosphors possess anti-thermal quenching properties and are suitable for developing optical temperature sensors.