Initial Oxidation Behavior of AlCoCrFeNi High-Entropy Coating Produced by Atmospheric Plasma Spraying in the Range of 650 °C to 1000 °C.

As protective coatings for the thermal parts of aero-engines, AlCoCrFeNi coatings have good application prospects. In this study, atmospheric plasma spraying (APS) was used to prepare AlCoCrFeNi high-entropy coatings (HECs), which were oxidized from 650 °C to 1000 °C. The mechanism of the oxide layer formation and the internal phase transition were systematically investigated. The results show that a mixed oxide scale with a laminated structure was formed at the initial stage of oxidation. The redistribution of elements and phase transition occurred in the HECs' matrix; the BCC/B2 structure transformed to Al-Ni ordered B2 phase and Fe-Cr disordered A2 phase.