Controlled Synthesis of Mg-MOF-74 and Its CO<sub>2</sub> Adsorption in Flue Gas

Yellow nanorod Mg-MOF-74 was obtained by solvothermal synthesis method. XRD、N2 adsorption-desorption isotherms、SEM and TGA results suggest that the particle size of Mg-MOF-74 reaches 400 nm after the introduction of sodium acetate in the precursor of Mg-MOF-74. Besides, the morphology of Mg-MOF-74 was changed from cauliflower to rod particles. At the same time, the BET specific surface area and pore volume of Mg-MOF-74 were also increased a lot. Then the CO2 dynamic adsorption capacity of Mg-MOF-74 was measured by self-made fix bed under 30 ℃、0.1 bar CO2 partial pressure. The results show that the CO2 adsorption capacity of Mg-MOF-74-N2 reaches 3.67 mmol/g and its CO2 adsorption capacity remains unchanged after 10 times CO2 adsorption-desorption cycles.