Carbonation of Dicalcium Silicate Enhanced by Ammonia Bicarbonate and Its Mechanism
Journal of Wuhan University of Technology-Mater. Sci. Ed.(2024)
摘要
The strength development law of γ -type dicalcium silicate ( γ -C 2 S) under different carbonation processes was investigated, and the carbonation mechanism of γ -C 2 S under the action of NH 4 HCO 3 was clarified by using a wide range of test methods, including XRD and SEM. A method of saturated NH 4 HCO 3 solution as a curing agent was identified to improve the carbonation efficiency and enhance the carbonation degree of γ -C 2 S, and then a high-strength carbonated specimen was obtained. Microhardness analysis and SEM morphology analysis were conducted on the carbonised specimens obtained under atmospheric pressure carbonisation conditions using the curing agent. It was found that γ -C 2 S could perform carbonisation well under atmospheric pressure, which promoted the carbonisation efficiency and decreased the carbonisation cost simultaneously. Therefore, a new carbonisation process solution was proposed for the rapid carbonisation of γ -C 2 S.
更多查看译文
关键词
γ-type dicalcium silicate,carbonization process,curing agent,atmospheric carbonization
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要