Influence of Pr-ion substitution in Cu₂X hexaferrites on their magnetic and dielectric properties

A series of Sr2Cu2PrxFe28-xO46 (x = 0.00 to x = 0.32 with a step of 0.08) hexagonal ferrite was synthesized by the heat treatment method, and heated at 1300 degree celsius for 6 h. These samples were characterized using FTIR, XRD, FESEM, VSM, and low-frequency (20 Hz-2 MHz) dielectric measurements. FTIR investigation confirms the ferrite phase formation in all the samples. XRD investigation reveals that all samples possess the X-type as a major phase with a minor M-phase. FESEM images show smaller grain size ranges between 25.27 mu m and 51.25 mu m. EDX elemental analysis confirms the existence of constituent elements in synthesized materials. VSM analysis shows that prepared ferrites possess a soft magnetic nature, the saturation magnetization of heated samples was found in the range of 35.99 Am-2/kg to 49.44 Am-2/kg, and coercivity was observed in the range of 10.372 kA/m to 37.443 kA/m. Relaxation peaks have been observed in the loss tangent profile for x = 0.00, 0.08. The Nyquist plot for samples S1 and S2 represents the low-loss universal capacitance circuit, while samples S3 to S5 represent the parallel conductance-capacitance circuit.