Exploitation of a New Nucleating Agent by Molecular Structure Modification of Aryl Phosphate and Its Effect on Application Properties of the Polypropylene

In this work, a novel alpha-nucleating agent (NA) for polypropylene (PP) termed APAl-3C-12Li was prepared and evaluated compared with the commercially available type NA-21. For the synthesis of the organophosphate-type NA (APAl-3C), the -OH group of the acid part of NA-21 was substituted by the isopropoxy group. The structure of APAl-3C was analyzed by spectroscopy and element analysis, the results of which were consistent with the theoretical molecular formula. APAl-3C's thermal stability was studied by differential scanning calorimetry (DSC) and thermogravimetry (TG), which showed only weak mass loss below 230 degrees C, meaning that it would not decompose during the processing of PP. The APAl-3C-12Li was used as a novel nucleating agent, studying its effects on crystallization, microstructure, mechanical and optical properties. Tests were performed in a PP random copolymer at different contents, in comparison to the commercial NA-21. The composite with 0.5 wt% APAl-3C-12Li has a similar crystallization temperature of 118.8 degrees C as with the addition of 0.5 wt% NA-21. An advantage is that the composite with the APAl-3C-12Li has a lower haze value of 9.3% than the counterpart with NA-21. This is due to the weaker polarity of APAl-3C-12Li after the introduction of methyl and better uniform dispersion in the PP matrix, resulting in stronger improvement of optical and mechanical properties.