4D evolutions of cracks, voids, and corrosion products in reinforced concrete materials.

This research paper presents a comprehensive investigation into the corrosion process in reinforced concrete structures using advanced analytical techniques, namely non-destructive X-ray computed tomography (CT) imaging, scanning electron microscopy (SEM) images, energy dispersive x-ray spectrometry (EDS), and Raman spectroscopy. The CT image analysis allowed for the identification and quantification of pore structures, crack propagation, and corrosion progression at different stages of corrosion. CT scanning and data analysis offer valuable 4D (3D spatial + time) insights into corrosion in reinforced concrete, revealing changes in pore sizes, with smaller pores increasing and larger pores decreasing as corrosion progresses. Our investigation reveals dynamic changes in reinforced concrete pores during the accelerated corrosion test leading to new pore formation and cracking. The research identifies two distinct types of cracks: one filled with corrosion products and the other, zipper-like cracks, resulting from the connection of deformed pores without corrosion products. The SEM images and EDS analysis confirmed the absence of corrosion products within these unique zipper cracks, suggesting a different mechanism of crack formation compared to the first type of cracks. The results revealed two distinct categories of corrosion products: iron oxides and iron hydroxides, with their distribution correlated to the duration of accelerated corrosion testing. The integration and verification of results from X-ray CT imaging and Raman spectroscopy established a comprehensive understanding of corrosion-induced damage in the reinforced concrete specimen, shedding light on complex interactions among different corrosion products during the corrosion process. These findings offer crucial insights for better understanding of the corrosion process in reinforced concrete paving the way for future development of effective treatments and strategies to mitigate corrosion impact.