Significantly enhanced fatigue resistance and mechanisms of hypoeutectic Al-Si composite calibrated using trace in-situ nanocrystals

Fatigue resistance under extreme stress conditions is an important indicator to evaluate industrial application potential of Al-Si-Mg alloys, but their fatigue resistance is inherently weakened by large grain size, long-needle Si phases and coarse precipitates. This work reports significantly optimized microstructure configuration and fatigue resistance of hypoeutectic Al-Si composite optimized by the nanocrystallization products of a NiNbTi metallic glass. It was proved the in-situ NiTi (B2) nanocrystals can serve as the heterogeneous nucleation sites of alpha-Al and P-Mg2Si and the growth retarder of eutectic Si. Particularly, the optimized composite exhibited nearly 5 times and 6 times longer fatigue life than the unoptimized alloy at 120 MPa (60 Hz) and 240 MPa (20 Hz), respectively. The fatigue strength (N = 107) was increased by 21.7 % and 25.9 % at 60 Hz and 20 Hz, respectively. The alpha-Al refinement enhanced the resistance to fatigue crack initiation. The refinement and spheroidization of eutectic Si phases reduced stress concentration. Also, the austenite-martensite phase transformation of NiTi afforded more energy for precipitation. Refined P-Mg2Si and P" phases were facilitated to interact with dislocations, improving the resistance to dislocation slip during cyclic strain through the dislocation shearing effect. This work provides a theoretical basis for the future development of Al-Si alloys and composites with excellent fatigue resistance for expanding their industrial application scope.