Preparation of Cold Sprayed Titanium TA2 Coating by Irregular Powder and Evaluation of Its Corrosion Resistance

Titanium coating on a steel substrate by surface technology can improve the corrosion resistance of steel. In this paper, the titanium TA2 coating was deposited on X80 steel by cold spraying equipment with a low-cost irregular powder. The effects of the carrier gas temperature on the microstructure, microhardness, wear resistance, adhesion and corrosion resistance of titanium coatings, especially in a deep sea environment, were studied by methods of porosity analysis, thermal field emission scanning analysis, energy spectrum analysis, Vickers hardness tests, bonding strength tests, friction and wear tests and electrochemical tests. The results showed that as the carrier gas temperature increased from 300 degrees C to 900 degrees C, the porosity of the coating decreased to 0.93%, and the hardness and bonding strength of the coating increased to 247 HV0.5 and 46.7 MPa, respectively. With the increase in hydrostatic pressure from 0.1 MPa to 40 MPa, the dimensional blunt current density of the titanium coating with 0.93% porosity was still in the order of 10-7 A center dot cm-2 with the cast titanium TA2.