Effects of the reaction temperature and Ba/Ti precursor ratio on the crystallite size of BaTiO3 in hydrothermal synthesis
RSC Advances(2022)
摘要
Nanocrystalline BaTiO3 has been prepared by hydrothermal synthesis from titanium isopropoxide and barium hydroxide octahydrate. Reaction conditions including synthesis temperature and Ba/Ti precursor ratio have been explored with the aim of producing BaTiO3 with small crystallites and a low concentration of defects. It has been found that the crystallite/particle size and tetragonality of the BaTiO3 samples increase as the synthesis temperature increases; and the crystallite/particle size of BaTiO3 is also affected by the Ba/Ti precursor ratio. The BaTiO3 sample synthesised using a Ba/Ti precursor ratio of 2 : 1 at a reaction temperature of 120 °C exhibited homogeneous crystallites of the smallest size of 107 nm. Additionally, the Ba/Ti precursor ratio of 2 : 1 with synthesis temperature of 220 °C was found to produce a smaller concentration of defects in BaTiO3.
更多查看译文
关键词
crystallite size,reaction precursor ratio,reaction temperature,batio<sub>3</sub>,synthesis
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要