Appearance of ferromagnetism in Pt(100) ultrathin films originated from quantum-well states with possibility of small orbital magnetic moment

Ferromagnetism was observed in a Pt(100) ultrathin film deposited on a SrTiO3(100) substrate. The ferromagnetism, which appears in films with thicknesses of 2.2-4.4 nm, periodically changes with a period of approximately 1 nm (5-6 ML) depending on the film thickness. This is consistent with the period derived from the quantum-well states formed in the thin film. X-ray magnetic circular dichroism measurements were conducted to understand the intrinsic nature of the ferromagnetism in the Pt(100) ultrathin films, and contrary to our expectations, the orbital magnetic moment of pure Pt is much smaller than that of the Pt/ferromagnetic multilayer system. These results suggest that the origin of the large magnetic anisotropy in Pt components cannot be explained only by the amount of spin-orbit coupling in Pt.