Effects of GBFS content and curing methods on the working performance and microstructure of ternary geopolymers based on high-content steel slag

Aimed to address the low utilization rate of steel slag (SS) and its challenge in resource utilization in China, this study developed ternary geopolymers made by high-content (50%) SS together with fly ash (FA) and granulated blast furnace slag (GBFS). The effects of GBFS content (0-40%) and curing methods (water curing, standard curing, sealed curing, and heat curing) on the working performance and microstructure of geopolymers were investigated. Microscopic analysis such as X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), thermogravimetric analysis (TG-DTG), and scanning electron microscopy (SEM) were utilized to investigate the hydration process and products of geopolymers under different curing conditions and GBFS content. The results indicated that when the GBFS content increased from 0% to 40%, the fluidity of the mixture decreased by 11.7%, the initial setting time of the geopolymer slurry decreased by 76%, and the geopolymer mortar's 28d compressive strength increased from 31.9 MPa to 60.6 MPa. At room temperature, the geopolymer mortar's 28d compressive strength was higher under standard curing (70.8 MPa) compared to water curing (57.5 MPa) and sealed curing (68 MPa). The geopolymer mortar cured at 60 degrees C for 24 h exhibited the highest 28d compressive strength (76.3 MPa). However, excessively high curing temperatures or prolonged durations led to more shrinkage cracks and reduced the compressive strength. The microscopic analysis revealed that the main gel products of ternary geopolymer were C-(A)-S-H gel. The amount of gel products is directly related to the strength of geopolymers. The developed ternary geopolymer has the potential to promote the large-scale utilization of SS in the concrete industry, making a significant contribution to sustainable development.