Electrochemical Performance of Nitrogen Self-Doping Carbon Materials Prepared by Pyrolysis and Activation of Defatted Microalgae

Pyrolysis and activation processes are important pathways to utilize residues after lipid extraction from microalgae in a high-value way. The obtained microalgae-based nitrogen-doped activated carbon has excellent electrochemical performance. It has the advantage of nitrogen self-doping using high elemental nitrogen in microalgae. In this study, two kinds of microalgae, Nanochloropsis and Chlorella, were used as feedstock for lipid extraction. The microalgae residue was firstly pyrolyzed at 500 degrees C to obtain biochar. Then, nitrogen-doped activated carbons were synthesized at an activation temperature of 700-900 degrees C with different ratios of biochar and KOH (1:1, 1:2, and 1:4). The obtained carbon materials presented rich nitrogen functional groups, including quaternary-N, pyridine-N-oxide, pyrrolic-N, and pyridinic-N. The nitrogen content of microalgae-based activated carbon material was up to 2.62%. The obtained materials had a specific surface area of up to 3186 m2/g and a pore volume in the range of 0.78-1.54 cm3/g. The microporous pore sizes of these materials were distributed at around 0.4 nm. Through electrochemical testing such as cyclic voltammetry and galvanostatic charge-discharge of materials, the materials exhibited good reversibility and high charge-discharge efficiency. The sample, sourced from microalgae Chlorella residue at activation conditions of 700 degrees C and biochar/KOH = 1:4, exhibited excellent endurance of 94.1% over 5000 cycles at 2 A/g. Its high specific capacitance was 432 F/g at 1 A/g.