Matching relationship research between ore and coke in thermal reserve zone under hydrogen-rich condition

In this paper, the mathematical relationship between the reduction degree of ore and the reaction rate constant k of FeO was established by experiments. Based on the unreacted core model, the relationship between the gas utilization rate in the thermal reserve zone (TRZ) and k and temperature is derived. The results show that with the decrease of the temperature in the TRZ, the gas utilisation rate increases first and then decreases. With the increase of the reduction degree of raw materials, the gas utilisation rate increases and the peak temperature decreases. With the increase of H2 content, the peak temperature increases. Finally, the relationship between coke reactivity and ore reduction degree and H2 content is: CRI = 164.88 In(RI) - 0.42 & phi;(H2)% - 696.18. By changing the matching relationship between ore and coke, the gas utilisation rate can be increased by 0.85% and the fuel ratio can be reduced by 5.70 kg & BULL;t-1 Dans cet article, on a etabli la relation mathematique entre le degre de reduction du minerai et la constante de vitesse de reaction k de FeO en utilisant le four de reduction pour reduire le minerai de fer et FeO. Sur la base du modele du noyau non reagi, on a deduit le changement du taux d'utilisation du gaz dans la zone de reserve thermique (TRZ) a differentes temperatures pour la reduction de FeO par le melange gazeux CO et H2, differentes compositions de gaz et differentes constantes de vitesse de reaction. Les resultats montrent qu'avec la diminution de la temperature dans la TRZ, le taux d'utilisation du gaz augmente d'abord et ensuite diminue. Avec l'augmentation du degre de reduction des matieres brutes, le taux d'utilisation du gaz augmente et la temperature de pointe diminue. A mesure que la proportion de H2 dans le melange de gaz augmente, le taux d'utilisation du gaz augmente legerement et la temperature de pointe augmente. L'amelioration de la reactivite du coke peut reduire la temperature de la TRZ, afin d'ameliorer le taux d'utilisation du gaz. Finalement, la relation entre la reactivite du coke et le degre de reduction du minerai et la teneur en H2 est: CRI = 164.88 ln(RI) - 0.42 & phi;(H2)% - 696.18. Dans les conditions existantes de la matiere brute, en modifiant la relation d'appariement entre le minerai et le coke, on peut augmenter le taux d'utilisation du gaz par 0.85% et reduire le rapport de combustible par 5.70 kg & BULL;t-1.