Fatigue life prediction of Ti60 titanium alloy under very high cycle loading at different temperatures

The very high cycle fatigue crack initiation mechanism of Ti60 titanium alloy at different temperatures was studied. The results showed that the initiation of cracks occurred on oversized facets in the subsurface. Based on this crack initiation mechanism, a full-life prediction model based on crack propagation at room temperature was first proposed, and then a very high cycle fatigue life prediction model considering temperature was proposed based on the degradation law of tensile strength at different temperatures. The experimental and predicted life results of Ti60 specimen at room temperature with 300 degrees C and 500 degrees C showed that the proposed method can effectively predict the very high cycle fatigue life, and the error is within a factor of 3.